Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..
Preheat temp. to 800 °C
Casting temperature 1350,00 °C
Liquidustemp. 1280 °C
Solidustemp 1210 °C
Composition Ni 64,6 · Cr 22,0 · Mo 10,0 · Si 2,1 · B · Mn · Nb
Density g/cm³ 8,2 g/cm³
Tensile strength 860 MPa
Color code 8
Content/amount 1 kg pack
Base metall Nickel
Elongation at break 9 %
Iso type I..
Composition: Co 63.0, Cr 30.0, Mo 5.0, Si 1.0, Mn 1.0, C
Base Metal: Cobalt
Color Code: 8
Preheat Temperature:
From: 950 °C
To: 1050 °C
Casting Temperature: 1420 °C
Solidus Temperature: 1270 °C
Liquidus Temperature: 1400 °C
Vickers Hardness: 385 HV10
..