Composition: Co 63.0, Cr 30.0, Mo 5.0, Si 1.0, Mn 1.0, C
Base Metal: Cobalt
Color Code: 8
Preheat Temperature:
From: 950 °C
To: 1050 °C
Casting Temperature: 1420 °C
Solidus Temperature: 1270 °C
Liquidus Temperature: 1400 °C
Vickers Hardness: 385 HV10
..
Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..
Preheat temp. to 800 °C
Casting temperature 1350,00 °C
Liquidustemp. 1280 °C
Solidustemp 1210 °C
Composition Ni 64,6 · Cr 22,0 · Mo 10,0 · Si 2,1 · B · Mn · Nb
Density g/cm³ 8,2 g/cm³
Tensile strength 860 MPa
Color code 8
Content/amount 1 kg pack
Base metall Nickel
Elongation at break 9 %
Iso type I..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: black..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: green..
Very thin and extremely flexible, they can be used for all dental alloys
Especially well-suited for the partial denture technique, for finishing areas that are difficult to access as well as for crown and bridge work – for example, for interdental work because they conform very closely to the shape ..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 6.5 x 24 mm, colour: black..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 15.5 mm, colour: black..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 15.5 mm, colour: green..
Futura Standard is a high copper non gamma-2 amalgam alloy based on a mixture of irregular atomized and lathe cut particles, especially designed for out-standing corrosion resistance and lowest creep value. Ardent Amalgam is CE marked through TUEV SUED, Germany.Clinical indications
Stress-bearing ..
Futura Plus is a dispersed phased non gamma-2 amalgam alloy with high silver content, especially designed for outstanding marginal integrity.
Ardent Amalgam is CE marked through TUEV SUED, Germany.Clinical indications
Stress-bearing occlusal restorations in the posterior area (class I and II).Co..
Futura Plus is a dispersed phased non gamma-2 amalgam alloy with high silver content, especially designed for outstanding marginal integrity.
Ardent Amalgam is CE marked through TUEV SUED, Germany.Clinical indications
Stress-bearing occlusal restorations in the posterior area (class I and II).Co..
Universal phosphate bonded casting investment material for model crown nand bridgework as well as casting technique by quick or progressive nheating procedure and for pressable ceramics Indications: crowns and bridgeworks, Co-Cr model castings, high-quality combination worksPacking: Univecast powder..
Type IV, Die stone, Special For CAD/Cam techniqueAdditional product information:
Mixing ratio 20 ml : 100 g
Mixing time (mechanical) 60 s
Processing time appr. 9-10 min.
Setting time appr. 13-14 min.
Hardness 24 h > 300 N/mm²
Hardness 30/60 min appr. 210/280 N/mm²
Compressive strength 1/24 h appr...