Special formula made up of high quality raw materials.
For general use on all alloys.
Optimum polishing effect with Polisoft pre-polishers and Bison brushes...
Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..
2-step polishing system for high shine on all composite materials
Polishers specifically adapted to each processing step
Best results even on very hard composites..
Endodontic Uses
Consepsis antibacterial solution is recommended for procedural endodontic disinfection, as a final endodontic rinse prior to canal obturation,1–3 and prior to pulp capping. Consepsis solution should be used after smear layer removal for canal disinfection. Sodium hypochlorite and EDT..
Diamond polishing paste specifically for high-gloss polishing of hybrid materials, for extra-oral use. Optimal polishing result thanks to diamond particles in the polishing paste that are specially matched to hybrid materials. Reduced plaque build-up and longer service life of the tooth restorations..
Composition: Co 63.0, Cr 30.0, Mo 5.0, Si 1.0, Mn 1.0, C
Base Metal: Cobalt
Color Code: 8
Preheat Temperature:
From: 950 °C
To: 1050 °C
Casting Temperature: 1420 °C
Solidus Temperature: 1270 °C
Liquidus Temperature: 1400 °C
Vickers Hardness: 385 HV10
..
The patented metal-ceramic material, IPS Style offers dental labs maximum efficiency, easy handling and life-like esthetics. This is the first material in the history of dental ceramics to contain oxyapatite crystals. These crystals reflect a high amount of incident lighting and provide restorations..
Preheat temp. to 800 °C
Casting temperature 1350,00 °C
Liquidustemp. 1280 °C
Solidustemp 1210 °C
Composition Ni 64,6 · Cr 22,0 · Mo 10,0 · Si 2,1 · B · Mn · Nb
Density g/cm³ 8,2 g/cm³
Tensile strength 860 MPa
Color code 8
Content/amount 1 kg pack
Base metall Nickel
Elongation at break 9 %
Iso type I..