Setting time (vicat-time) 6 min
Product description Universal investment material
Compressive strength 11 MPa
Linear thermal expansion 0,8 %
Flowability 140 mm
Content/amount 18 kg (45 x 400 g bag)
Processing time at 22°C ca. 3:30 min
Very good flowing and modeling characterisitics due to a wide
melting range.
Highly precise fitting accuracy due to very low shrinkage.
Ideally suited..
Depending on the alloy and the field of application, the required mixing ratio can be created for these liquids using distilled or demineralised water..
Depending on the alloy and the field of application, the required mixing ratio can be created for these liquids using distilled or demineralised water..
Setting time (vicat-time) ca. 10 min
Product description Precision casting investment material for crown & bridge techniques
Linear thermal expansion ..
The rounded upper edge and concave shape facing the tongue plus the anatomical lower-jaw profile make for good patient acceptance
Tip: For periodontal..
Depending on the alloy and the field of application, the required mixing ratio can be created for these liquids using distilled or demineralised water..
Depending on the alloy and the field of application, the required mixing ratio can be created for these liquids using distilled or demineralised water..