WIROBOND 280 Cobalt-Chromium alloy for crowns & bridges 1Kg

Preheat temp. to 1000 °C Preheat temp. from 900 °C Composition Co 60,2 · Cr 25,0 · W 6,2 · Mo 4,8 · Ga 2,9 · Mn · Si Solidustemp 1355 °C Liquidustemp. 1430 °C Product description Cobalt-Chromium alloy for crowns & bridges Vickershardness 280 HV10 Casting temperature 1500 °C Color code 8 Base metall Cobalt Content/amount 1 kg pack Yield strength 515 MPa Tensile strength 680 MPa Elongation at break 14 % Density g/cm³ 8,2 g/cm³ Elastic modul 215 GPa