Self-curing composite material for the fabrication of provisional crowns and bridgesIndications:
Fabrication of aesthetic temporary crowns, bridges, inlays and onlaysAdvantages:
Simple and fast working steps
Less than 1 minute setting time in the mouth
Easy to shape and polish
Available in 8 sha..
Fast setting temporary bis-acrylic crown and bridge material in 1:1 cartridge. All purpose, economical self-curing material for fabrication of temporary crowns, bridges, inlays and onlays.
Simple and fast working
Less than 1 minute set time in mouth
Easy to shape and polish
Available in 8 shades for..
Self-curing composite material for the fabrication of provisional crowns and bridgesIndications:
Fabrication of aesthetic temporary crowns, bridges, inlays and onlaysAdvantages:
Simple and fast working steps
Less than 1 minute setting time in the mouth
Easy to shape and polish
Available in 8 sha..
Fast setting temporary bis-acrylic crown and bridge material in 1:1 cartridge. All purpose, economical self-curing material for fabrication of temporary crowns, bridges, inlays and onlays.
Simple and fast working
Less than 1 minute set time in mouth
Easy to shape and polish
Available in 8 shades for..
Self-curing composite material for the fabrication of provisional crowns and bridgesIndications:
Fabrication of aesthetic temporary crowns, bridges, inlays and onlaysAdvantages:
Simple and fast working steps
Less than 1 minute setting time in the mouth
Easy to shape and polish
Available in 8 sha..
Fabrication of temporary crowns, bridges, inlays, onlays, partial crowns, veneers and temporary posts
Fabrication of long-term temporaries
Lining of pre-fabricated temporary crowns made from composite materials, polycarbonate or metal
quick, simple and reliable thanks to the 1:1 cartridge syst..
Fabrication of temporary crowns, bridges, inlays, onlays, partial crowns, veneers and temporary posts
Fabrication of long-term temporaries
Lining of pre-fabricated temporary crowns made from composite materials, polycarbonate or metal
quick, simple and reliable thanks to the 1:1 cartridge syst..
Fabrication of temporary crowns, bridges, inlays, onlays, partial crowns, veneers and temporary posts
Fabrication of long-term temporaries
Lining of pre-fabricated temporary crowns made from composite materials, polycarbonate or metal
quick, simple and reliable thanks to the 1:1 cartridge syst..
1 pair plastic inserts autaclavable up to 180°C For the removal of crowns and bridges. For a better grip, tip of pliers can be enhanced with rubber packing and emery powder..
Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..