Preheat temp. to 800 °C
Casting temperature 1350,00 °C
Liquidustemp. 1280 °C
Solidustemp 1210 °C
Composition Ni 64,6 · Cr 22,0 · Mo 10,0 · Si 2,1 · B · Mn · Nb
Density g/cm³ 8,2 g/cm³
Tensile strength 860 MPa
Color code 8
Content/amount 1 kg pack
Base metall Nickel
Elongation at break 9 %
Iso type I..
Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..
ProTaper Ultimate Rotary Files are a cutting-edge solution for root canal treatment, designed to deliver exceptional results through the integration of the latest generation of ProTaper NiTi files, enhanced disinfection techniques, and dedicated obturation methods. This comprehensive system works se..
Futura Standard is a high copper non gamma-2 amalgam alloy based on a mixture of irregular atomized and lathe cut particles, especially designed for out-standing corrosion resistance and lowest creep value. Ardent Amalgam is CE marked through TUEV SUED, Germany.Clinical indications
Stress-bearing ..
Composition: Co 63.0, Cr 30.0, Mo 5.0, Si 1.0, Mn 1.0, C
Base Metal: Cobalt
Color Code: 8
Preheat Temperature:
From: 950 °C
To: 1050 °C
Casting Temperature: 1420 °C
Solidus Temperature: 1270 °C
Liquidus Temperature: 1400 °C
Vickers Hardness: 385 HV10
..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: green..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 6.5 x 24 mm, colour: black..
Non-Water Soluble
The die:master system provides you with perfect die preparation as a working basis for conventional and all-ceramic restorations.
Optimally prepared and protected working base with coordinated system components.
Hard-wearing die surface due to specially developed plaster hardener a..
Very thin and extremely flexible, they can be used for all dental alloys
Especially well-suited for the partial denture technique, for finishing areas that are difficult to access as well as for crown and bridge work – for example, for interdental work because they conform very closely to the shape ..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: black..