Grandio, Universal Composite Syringe 4g, A2

Grandio, Universal Composite Syringe 4g, A2 - VOCO - 1811
Top Quality 30 Days Delivery
Grandio, Universal Composite Syringe 4g, A2
217.80 SR
Ex Tax: 217.80 SR
  • Type: Nano-Hybrid
  • Tooth: Anterior + Posterior
  • Class: Universal
  • Shade: A2
  • Packing: Syringe 4g

Grandio is a state-of-the-art, light-curing nano-hybrid composite designed for versatile dental restorative procedures. Developed using advanced nano-technology, it offers a balance of high physical strength and easy handling, ensuring long-lasting restorations with excellent aesthetics.

Nano-Technology: Grandio incorporates nano-particles for a densely packed composite, ensuring high strength and minimal shrinkage.

Key Features:

  • Composition: Nano-hybrid composite with 87% w/w high filler content.
  • Consistency: Smooth, non-tacky, easily moldable, facilitating quick adaptation to tooth morphology.
  • Polymerisation Shrinkage: Significantly reduced at 1.57%, minimizing stress on cavity walls.
  • Cure Time: 20 seconds exposure for efficient processing.
  • Abrasion Resistance: Extremely high, with a surface hardness of 285 MHV.
  • Elasticity: E-modulus of 17.1 GPa, similar to natural dentine.
  • Thermal Expansion: Comparable to tooth substance (α = 19 [10^-6/K]).
  • Shades: Available in 16 shades with a guide made from the original material.


  • Durability: Pronounced abrasion resistance and chewing stability.
  • Aesthetics: Natural-looking restorations with tooth-like translucency.
  • Versatility: Suitable for Class I - V fillings, aesthetic corrections, splinting, and more.
  • Compatibility: Works with all dentine/enamel bonding agents.


  • Class I to V fillings
  • Reconstruction of traumatically affected anteriors
  • Facetting of discoloured anteriors
  • Correction of shape and shade for better aesthetic appearance
  • Locking, splinting of loose teeth
  • Repairing veneers
  • Filling deciduous teeth
  • Core-build-up under crowns
  • Composite inlays

Product Specifications:

Clinical Evidence: Referenced by Dr. H. Wolter at the Fraunhofer-Institute for Silicate Research ISC, 2005.

Filler Content87% w/w
Polymerisation Shrinkage1.57%
Surface Hardness (MHV)285
Cure Time20 seconds
E-modulus (GPa)17.1
Thermal Expansion (α)19 [10^-6/K]
Available Shades16