Composition: Co 63.0, Cr 30.0, Mo 5.0, Si 1.0, Mn 1.0, C
Base Metal: Cobalt
Color Code: 8
Preheat Temperature:
From: 950 °C
To: 1050 °C
Casting Temperature: 1420 °C
Solidus Temperature: 1270 °C
Liquidus Temperature: 1400 °C
Vickers Hardness: 385 HV10
..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: black..
Preheat temp. to 800 °C
Casting temperature 1350,00 °C
Liquidustemp. 1280 °C
Solidustemp 1210 °C
Composition Ni 64,6 · Cr 22,0 · Mo 10,0 · Si 2,1 · B · Mn · Nb
Density g/cm³ 8,2 g/cm³
Tensile strength 860 MPa
Color code 8
Content/amount 1 kg pack
Base metall Nickel
Elongation at break 9 %
Iso type I..
Preheat temp. from 900 °C
Preheat temp. to 1000 °C
Density g/cm³ 8,3 g/cm³
Iso type ISO22674 3
Base metall Nickel
Elastic modul 170
Yield strength 335 MPa
Tensile strength 655 MPa
Elongation at break 43 %
Content/amount 1 kg pack
Vickershardness 195 HV10
Liquidustemp. 1360 °C
Casting temperature 145..
Special formula made up of high quality raw materials.
For general use on all alloys.
Optimum polishing effect with Polisoft pre-polishers and Bison brushes...
Very thin and extremely flexible, they can be used for all dental alloys
Especially well-suited for the partial denture technique, for finishing areas that are difficult to access as well as for crown and bridge work – for example, for interdental work because they conform very closely to the shape ..
The Rinn Megalloy EZ Amalgam Capsules are a dental restorative material commonly used in dental practices. These capsules contain a pre-proportioned blend of alloy and mercury, designed for the creation of dental amalgam, a material used for filling cavities.Composition Spill 1The capsules typi..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 22 x 3.5 mm, colour: green..
The Rinn Megalloy EZ Amalgam Capsules are a dental restorative material commonly used in dental practices. These capsules contain a pre-proportioned blend of alloy and mercury, designed for the creation of dental amalgam, a material used for filling cavities.Composition Spill 2The capsules typi..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 6.5 x 24 mm, colour: black..
The Rinn Megalloy EZ Amalgam Capsules are a dental restorative material commonly used in dental practices. These capsules contain a pre-proportioned blend of alloy and mercury, designed for the creation of dental amalgam, a material used for filling cavities.Composition Spill 3The capsules typi..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 15.5 mm, colour: black..
For pre-polishing the surfaces of precious and non-precious castings which can then be high-lustre polished to a deep, lasting lustreper minute 10000 min
Content/amount 100 pieces
Product description Ø 15.5 mm, colour: green..